Synthetic resin
.jpg)
Synthetic resin
Synthetic resin is colorless transparent to light yellow product. It is suitable for solvent type coating and printing ink, no-solvent type coating, powder coating and resin modified. It can effectively improve paint film, shorten drying time, promote hardness and etc. In brief, it is widely applied in paint, coating and printing ink fields.
Performance parameter
|
Item
|
Standard index
|
Testing standard
|
|
A81
|
A101
|
|
appearance
|
white or light yellow transparent solid
|
|
|
softening point ℃
|
85~105
|
100~130
|
DIN(53180)
|
|
chromaticity(iodine colorimetry)
|
≤1
|
≤1
|
DIN(6162)
|
|
acid value(mgkoH/g)
|
≤2
|
≤2
|
DIN(53402)
|
|
hydroxyl value(mgKOH/g)
|
40~70
|
40~70
|
ISO4629
|
Synthetic resin uses
This product is mainly used coating industry, printing ink industry and adhesion agent field.
A.Printing ink industry
|
Uses
|
Dosage
|
| Used in plastic surface printing ink, plastic compound printing ink, aluminium foil printing ink, gold blocking printing ink, paperboard printing ink, anti-forgery ink, transparent ink, heat transfer printing ink to improve glossiness, adhesive force, levelling property and drying capacity |
recommended 3%-5% |
| Used in solvent type gravure, flexography and silk-screen printing to improve pigment wettability, glossiness and solid content |
recommended 3%-8% |
| Used in cigarette case oil polish, paper oil polish, leather oil polish, shoes oil polish, fingermail oil polish, tipping paper printing ink to improve glossiness, adhesive force, drying property and printing property |
recommended 5%-10% |
| Used in ball-point pen printing ink to endow it with specialrheological property |
|
| Used in high temperature resistant milk carton printing ink and in other system |
recommended 1%-5% |
| Used in ink, lakes, fiber type printing ink, excellent water proofing property |
|
| Mixed with styrene and modified crylic acid to manufacturing copying machine used toner |
|
B.Coating industry
|
Uses
|
Dosage
|
| In manufacturing of wood varnish or color paint and wood primer |
Dosage 3%-10% |
| Used in nitro metallic paint to promote solid content, glossiness, adhesive force; as mechanical finishing coat, primer and refinishing paint; having strong adhesive force on steel, copper, aluminum and zinc |
Dosage 5% |
| Used in cellulose nitrate or acetylcellulose paper coating to improve fast drying, whiteness, glossiness, flexibility, wear resistance and elasticity |
Dosage 5% |
| Used in baking paint to improve drying speed |
Dosage 5% |
| Used in chlorinated rubber paint and vinyl chloride copolymer paint to reduce viscosity, improve adhesive force |
replace base stock by 10% |
| Used in polyurethane system to improve water proofing property, heat resistance and corrosion resistance |
Dosage 4～8% |
| Suitable for nitrolacquer, plastic coating, acrylic resin paint, hammer paint, automobile varnish, automobile repair paint, motorcycle paint, bicycle paint |
Dosage 5% |
C. Adhesive field
1.Synthetic resin is suitable for cellulose nitrate adhesive used in bonding of textiles, leather, paper and other material.
2.Synthetic resin is applied in hot melting compound with butyl acetoacetic cellulose due to excellent heat stability to control melt viscosity and hardness of cooling block.
3.Synthetic resin is soluble in ethyl alcohol and is with certain hardness. It is suitable for manufacturing of polishing agent and wood surface treating agent.
4.Synthetic resin is used as textile water-proofing agent in cleaning.
5.Synthetic resin is used in polyurethane component adhesive to improve adhesion fastness, brightness, water proofing property and weather fastness.
|